High-Temperature Co-fired Ceramic (HTCC) Tapes

Product Purpose PDF Datasheet Add to
Quote
44009

A 96% alumina, high temperature co-fired ceramic (HTCC) tape. This material can be co-fired with platinum or other base metal at 1500°C to give a dense white colored ceramic.

44009 Datasheet Add 44009 to RFQ
44007

A 99.99% alumina, high temperature co-fired ceramic (HTCC) tape. This material can be co-fired with platinum or other base metal at 1550°C to give a dense white colored ceramic.

44007 Datasheet Add 44007 to RFQ
49000

A fugitive tape that is designed to be co-fired with zirconia or alumina green tape for use in planar oxygen sensors. This material is designed to be burned out in the temperature range of 600°C to 700°C.

49000 Datasheet Add 49000 to RFQ
49010

A monoclinic zirconia for use as a release liner between green ceramic parts and kiln furniture during firing process.

49010 Datasheet Add 49010 to RFQ
42421

A high temperature co-fired ceramic (HTCC) that is a blend of nickel oxide and yttria stabilized zirconia. This material is co-fired with nickel oxide support anode and zirconia electrolyte to form the function anode in an anode supported solid oxide fuel cells (SOFC).

42421 Datasheet Add 42421 to RFQ
42401

A high temperature co-fired ceramic (HTCC) fully stabilized zirconia (8 mol.% yttria) tape that is 125 microns in thickness. This material is fired between 1450°C and 1550°C to form the electrolyte in an electrolyte supported solid oxide fuel cells (SOFC).

42401 Datasheet Add 42401 to RFQ
42420

A high temperature co-fired ceramic (HTCC) that is a blend of nickel oxide and yttria stabilized zirconia. This material is co-fired with nickel oxide support anode and zirconia electrolyte to form the function anode in an anode supported solid oxide fuel cells (SOFC).

42420 Datasheet Add 42420 to RFQ
42000

A high temperature co-fired ceramic (HTCC) partially stabilized zirconia (3 mol.% yttria) tape that is used in pressure sensors. This material is fired between 1400°C and 1500°C to give a dense white colored ceramic.

42000 Datasheet Add 42000 to RFQ
42020

A high temperature co-fired ceramic (HTCC) partially stabilized zirconia (5 mol.% yttria) tape that is used in planar oxygen sensors. The material is co-fired with platinum pastes between 1450°C and 1550°C to yield a dense white colored ceramic.

42020 Datasheet Add 42020 to RFQ
42400

A high temperature co-fired ceramic (HTCC) fully stabilized zirconia (8 mol.% yttria) tape that is 15 microns in thickness. This material is co-fired with nickel oxide tapes between 1450°C and 1550°C to form the electrolyte in an anode supported solid oxide fuel cells (SOFC).

42400 Datasheet Add 42400 to RFQ